Аннотация:Weld filler alloys that exploit transformation plasticity through low austenite to martensite transformation temperatures offer an effective method of reducing residual stresses in strong steel welds. However, in multipass welds, the heat input from later weld passes may be insufficient to retransform prior welding passes, leading to the accumulation of thermally induced strains and elevated residual stresses. In this work, the residual stress distributions produced around arc welds fabricated with a martensitic weld filler alloy that transforms at a low temperature have been studied as a function of the number of passes deposited and the interpass temperature. It is found that when the interpass temperature is above the transformation temperature of the weld metal, the entire multipass weld transforms as a single entity, thus permitting the optimum exploitation of the transformation plasticity. In contrast, the deposition of new metal with a relatively low interpass temperature leads to increased residual stresses in the underlying layers, reducing or eliminating the beneficial stress states previously created.