Аннотация:The formation of precipitates of Ti and Cr nitrides in cold-rolled Fe + Ni(4at%) Ti(2at%) and Fe + Ni(4at%) + Cr(3at%) after a pre-nitriding step was investigated by M?ssbauer spectroscopy (MS) and transmission electron microscopy (TEM). From MS data we conclude that initially most of the Ti and Cr were atomically dispersed. Using TEM and high-resolution TEM (HRTEM), we found that the Baker-Nutting (B-N) orientation relationship (OR) holds for platelets one to two interatomic distances thick, producing streaking around the (200) reflections, while for thicker precipitates the Nishiyama-Wasserman (N-W) OR is more favorable. We also observed a transient phase, Cr2N, the formation of which was possible due to the relatively low nitriding temperature, a low nitriding potential, and the presence of Cr inclusions of relatively large initial size.