In this work, a task was set to study the rheological properties of zircon-based alloys with a
modified chemical composition of the Zr – Nb and Zr – Nb – Sn systems with respect to the
conditions of different processes of pressure metal treatment during manufacturing of pipes
and rods. For this purpose, complex plastometric tests of new grades of alloys were carried out
to obtain experimental data on the deformation resistance value σp and maximum permissible
plasticity Λр of these materials. The tests were carried out on a modern plastometric apparatus
in a wide range of thermal mechanical conditions of deformation according to different forms
of loading. On the basis of the experimental data on the mechanical properties of the materials
under study, pressure metal treatment processes were developed using the Forge 2008 computer
modeling software package. В настоящей работе поставлена задача исследования реологических свойств
модифицированных по химическому составу сплавов циркония систем Zr – Nb и Zr – Nb – Sn
применительно к условиям различных процессов обработки металлов давлением (ОМД) при
производстве труб и прутков. Для этого были выполнены комплексные пластометрические
исследования новых марок сплавов с целью получения экспериментальных данных по
величине сопротивления деформации σs и предельной пластичности Λр этих материалов.
Испытания проводились на современной пластометрической установке в широком
диапазоне термомеханических условий деформирования по различным законам нагружения.
На основе экспериментальных данных о механических свойствах исследуемых материалов
осуществлена разработка режимов технологических процессов ОМД с использованием
программного комплекса для компьютерного моделирования Forge 2008