Biodegradation ability of synthetic polymer materials is an urgent problem of modern ecology
situation. A known new biodegradable polymer is polyangelicalactone (PAL). In this paper, styrene-α-
angelicalactone copolymers were obtained by radical polymerization. The resulting copolymers have
physical and mechanical properties similar to those of polystyrene and its graft-copolymers
with PAL.
Both they were mechanically destroyed when incubated in gray forest soil over 28 weeks. The obtained
results show that the modification of polystyrene with the impurities of α-angelicalactone
does not
worsen the mechanical properties of the copolymers but instead gives them biodegradation abilities. В настоящей работе получены сополимеры стирола и α-ангеликалактона
методом
радикальной полимеризации. Полученные сополимеры имеют физико-механические
свойства,
аналогичные свойствам
полистирола и его привитых сополимеров с полиангеликалактоном. Оба
полимера механически разрушаются при инкубации в серой лесной почве в течение 28 недель.
Полученные результаты показывают, что модификация полистирола примесями α-ангеликалактона
не ухудшает механические свойства
сополимеров и придает им способность к биоразложению