Polyangelicalactone-graft-
polystyrene
copolymers (PAL‑graft-PS)
were obtained through
cationic polymerization. The resulting copolymers were completely destroyed when incubated in gray
forest soil over 28 weeks. Individual strains of fungi destroyed the copolymer partially within 13 weeks;
the most active among the studied cultures was Leptographium sp. The biodegradation products of
copolymers do not statistically have a toxic effect. The obtained results show that the modification of
polystyrene (PS) with the impurities of polyangelicalactone (PAL) gives them biodegradation abilities
and does not worsen the properties of the copolymers. Получены привитые сополимеры стирола с полиангеликалактоном (PAL‑graft-PS)
методом катионной полимеризации. Установлено, что сополимеры полностью разрушаются
при инкубации в серой лесной почве в течение 28 недель. Отдельные штаммы грибов
частично разрушали сополимер в течение 13 недель; среди изученных культур наиболее
активна Leptographium sp. Продукты биоразложения сополимеров и блок-сополимеров
статистически не обладают токсическим действием. Полученные результаты показывают, что
модификация полистирола (PS) примесями полиангеликалактона (PAL) придает им способность
к биоразложению, не ухудшая свойства
сополимеров