Self-compacting concrete is obtained by partial replacement of Portland cement with pre-prepared ash of rice husk. Preliminary preparation included heat treatment of ash under different conditions. The optimal preparation technology allowing to obtain a homogeneous concrete mixture. All mixtures with the replacement of cement with ash up to 25% meet the requirements for rheological characteristics and resistance to delamination. The increase in the ash content of rice husks led to a decrease in the early mechanical properties, while the final strength of self-compacting concrete containing ash was comparable to conventional samples. This was achieved due to the pozzolan activity of the ash. The inclusion of rice husk ash reduced the amount of portlandite in the system by obtaining additional C-S-H gel, which led to matrix compaction and blocking of open porosity networks.
Самоуплотняющийся бетон получен путем частичной замены портландцемента предварительно подготовленной золой рисовой шелухи. Предварительная подготовка включала в себя термическую обработку золы при различных условиях. Выявлена оптимальная технология приготовления, позволяющая получить гомогенную бетонную смесь. Все смеси c заменой цемента золой до 25 % отвечают требованиям к реологическим характеристикам и сопротивлению расслоению. Увеличение содержания золы рисовой шелухи привело к снижению ранних механических свойств, тогда как конечная прочность самоуплотняющегося бетона, содержащего золу, была сопоставима с обычными образцами. Это было достигнуто за счет пуццолановой активности золы. Включение золы рисовой шелухи уменьшило количество портландита в системе за счет получения дополнительного геля C-S-H, что привело к уплотнению матрицы и блокированию сетей с открытой пористостью.